rsos.royalsocietypublishing.org

Research Cite this article: Yen Y-C, Lin C-C, Chen P-Y, Ko W-Y, Tien T-R, Lin K-J. 2017 Green synthesis of carbon quantum dots embedded onto titanium dioxide nanowires for enhancing photocurrent. R. Soc. open sci. 4: 161051. http://dx.doi.org/10.1098/rsos.161051 Received: 23 December 2016 Accepted: 11 April 2017 Subject Category: Chemistry Subject Areas: green chemistry/materials science/nanotechnology Keywords: carbon quantum dot, titanium dioxide, water splitting, peroxide and photo catalyst Author for correspondence: Kuan-Jiuh Lin e-mail: [email protected] This article has been edited by the Royal Society of Chemistry, including the commissioning, peer review process and editorial aspects up to the point of acceptance. Electronic supplementary material is available online at https://dx.doi.org/10.6084/m9. figshare.c.3749912.

Green synthesis of carbon quantum dots embedded onto titanium dioxide nanowires for enhancing photocurrent Yin-Cheng Yen, Chia-Chi Lin, Ping-Yu Chen, Wen-Yin Ko, Tzu-Rung Tien and Kuan-Jiuh Lin Department of Chemistry, National Chung Hsing University, Taichung 402, Taiwan, Republic of China.

K-JL, 0000-0001-5830-1875 The green synthesis of nanowired photocatalyst composed of carbon quantum dots-titanium hybrid-semiconductors, CQDs/TiO2 , are reported. Where graphite-based CQDs with a size less than 5 nm are directly synthesized in pure water electrolyte by a one-step electrochemistry approach and subsequently electrodeposited onto as-prepared TiO2 nanowires through a voltage-driven reduction process. Electron paramagnetic resonance studies show that the CQDs can generate singlet oxygen and/or oxygen radicals to decompose the kinetic H2 O2 intermediate species upon UV light illumination. With the effect of peroxidase-like CQDs, photocurrent density of CQDs/TiO2 is remarkably enhanced by a 6.4 factor when compared with that of as-prepared TiO2 .

1. Introduction Titanium dioxide (TiO2 ) is one of the most attractive photocatalytic materials which has been used extensively for photo electrochemical related applications because of its high photo activity and excellent chemical stability as well as low cost [1,2]. However, current direct TiO2 nanomaterials for water splitting face many challenge issues: one is the wild band gap of TiO2 which limits the light harvest [3–8]. The other critical problem is the generated peroxide via a two-electron pathway will delay the release of oxygen and poison the activity of TiO2 [9– 11]. For longstanding application of TiO2 on water splitting, it is necessary to enlarge light harvest in the visible region and eliminate peroxides during the water splitting process. Traditionally, chemical doping and dye sensitizing are used

2017 The Authors. Published by the Royal Society under the terms of the Creative Commons Attribution License http://creativecommons.org/licenses/by/4.0/, which permits unrestricted use, provided the original author and source are credited.

2.1. Preparation of carbon quantum dot solution The graphite-coated rod (electron conductivity, 1.25 ohm cm−1 ; hardness, 64 Hs) was inserted into the ultra-pure water (18 M ohm cm−1 , 30 ml) as the anode, the Ag/AgCl as the reference electrode and the platinum wire as the counter electrode. The synthetic control parameters of cyclic voltammetry (CV) include that scan range of applied potential is +3 V to −3 V and scan rate is 0.5 V s−1 with 3500 cycles.

2.2. Preparation of CQDs/TiO2 NWs on FTO FTO (F:SnO2 ) (TEC-7, 8 ohm square) was cleaned by ultrasonic agitation in detergent, deionized water and a mixture solution of ethanol, acetone and deionized water with a volume ration of 1 : 1 : 1 for 15 min, respectively. The FTO substrates were immersed in an aqueous of 0.5 M TiCl4 (99%, Merck) at 80°C for 30 min and followed by heat treatment at 500°C for 30 min to generate a compact TiO2 layer. The TiCl4 treated substrates were then suspended in a reagent solution that contained 6 ml 2-butanone (more than 99%, Merck), 6 ml HCl (12 M, Merck) and 0.6 ml tetrabutyl titanate (more than 97%, Alderich) in a Telflon vessel. The telflon vessel was sealed in an autoclave and heated at 200°C for 1.5 h. After further annealing at 500°C for 30 min, the crystallinity of TiO2 NWs was grown on FTO substrates. The electrodeposition of CQDs onto TiO2 NWs was performed with a standard three-electrode system (electronic supplementary material, figure S1), consisting of a TiO2 NW electrode as the working electrode, Ag/AgCl as the reference electrode and platinum sheet as the counter electrode, at –3.0 V for 1 h.

2.3. Characterizations The morphology and lattice spacing images of CQDs and CQDs/TiO2 NWs were recorded by transmission electron microscopy (TEM, JEM-2010, JEOL) operated at 200 kV. The absorbance spectra were obtained with a UV/vis/NIR spectrometer (Lambda 900, Perkin Elmer). The photoluminescence

................................................

2. Material and methods

2

rsos.royalsocietypublishing.org R. Soc. open sci. 4: 161051

to enhance light absorption [12]. Furthermore, metal-catalyst [13–15], chemical agent [16] and physical bubbling methods [17] have been reported for removing the H2 O2. Unfortunately, there is lack of a solution to overcome all problems at once. Carbon quantum dots (CQDs) are a new kind of carbon nanostructure which have received wide attention owing to their unique properties of good biocompatibility, robust chemical inertness and high resistance to photobleaching [18–23]. Moreover, the optical properties of CQDs can be tuned by size control, chemical doping and functionalization for featured applications [24–27]. Recently, an interesting result was found that CQDs which could serve as peroxidase mimetics demonstrate an excellent catalytic activity on the decomposition of H2 O2 [28]. Liu et al. reported that metal-free CQD-carbon nitride nanocomposites serving as photocatalysts were explored to break the peroxide down [9]. These results provide an idea to develop CQD-containing hybrid semiconductors for solving toxic issues during the water splitting process. Generally, CQDs could be produced by traditional methods such as electrochemical oxidation, laser ablation, hydrothermal/solvothermal treatment, microwave irradiation and arc discharge [24,29]. Recently, a special chemical cleavage of layered N-doped carbon materials, carbon nitride quantum dots (CNQDs), was proposed [30]. Lately, the facile electrochemical fabrication of water-soluble CQDs has been achieved using an alkali-base (NaOH/EtOH) electrolyte [31]. Unfortunately, these processes require chemicals/surface passive agents, complex instrumental set-ups or post-treatments. To the best of our knowledge, one-step synthesis of homogeneously dispersed CQDs in pure water without using chemicals and further post-treatments is still challenged. Herein, we report a straightforward three-electrode electrochemical approach to produce high-quality CQDs in pure water electrolyte (i.e. without using acids and bases). This facial electrochemical fabrication offers a one-step technology to prepare CQD water solution without further post-treatments like filtration, dialysis, centrifugation, column chromatography and gel-electrophoresis. A hybrid photoactive anode that consists of CQDs and titanium dioxide nanowires (CQDs/TiO2 NWs) was fabricated for high efficient water splitting via an electrodeposition approach. Results revealed that the CQDs play a role of peroxidase to catalyse the transformation of H2 O2 into oxygen which leads to lower charge transfer resistance and ion diffusion resistance. Therefore, photocurrent density of CQDs/TiO2 NWs was remarkably enhanced by a 6.4 factor when compared to that of an as-prepared TiO2 NW photo anode.

The photograph of CQD solution is show in figure 1a. After 3500 scan cycles, the colour of the CQD’s solution is probably clear; however, a pale-green emission appeared gradually under UV light (365 nm) irradiation in the reactor. We have shown that the present one-step methodology is scalable, repeatable and of straightforward characterizations. The aqueous CQDs exhibited a typical UV-Vis absorption from 300 to 600 nm and a broad emission peaking at 500 mm, while excitation at 365 nm (figure 1b,c). Remarkably, the corresponding photoelectric properties of CQD solution remain unchanged after storing for 10 months in air at room temperature (electronic supplementary material, figure S2). From HRTEM images, as show in figure 1d,e, the size distribution of CQDs is from 0.5–4 nm and it presents an average lattice spacing of CQDs as 0.323 nm, corresponding to (002) planes of graphite [32,33]. It was reported that small graphite-like nanoparticles revealed excellent up-conversion luminescence properties and even generated singlet oxygen (1 O2 ) and/or oxygen radicals from water [34–36]. Accordingly, electron paramagnetic resonance (EPR) was employed to probe 1 O2 in CQD solution under UV irradiation by means of spin trap reagent, 5,5-dimethyl-1-pyrroline N-oxide (DMPO), which has been proposed to detect 1 O2 by readily forming [DMPO−1 O2 ] intermediately succeeded by quick decomposition into DMPO–OH radical as well as the equivalent hydroxyl radical [37]. The EPR spectra are highlighted in figure 2. Weak signals are observed before UV irradiation because of slight oxidation of DMPO arose by ambient visible light during sample preparation. Upon irradiation of 365 nm for 90 s, a highly intense signal with typical 1 : 2 : 2 : 1 DMPO/•OH peaks is consequently obtained, indicating that the extremely efficient production of 1 O2 and/or oxygen radicals is facilely induced by photo-activated CQDs in water solution. To further explore the photo-converse-electron efficiency of the CQD-embedded titanium dioxide system, we offer the voltage-driven reduction process for the growth of CQDs/TiO2 NWs. An HRTEM image of the growth of CQDs onto TiO2 NWs while electrodepositing at −3 V for 1 h is shown in figure 3a. It was observed that TiO2 NWs have a diameter of 30 nm and the dark dots in the TEM image represent the CQDs. Moreover, the distance between the adjacent lattice fringes is 0.325 nm and 0.223 nm, which can be assigned to the interplane distance of the rutile TiO2 (110) plane and (101) planes of graphite (JCPDS card: no. 65-6212) (electronic supplementary material, figure S3). Further characterization studies of Raman spectra provided convincing evidence for the graphite-based structure of CQDs on TiO2 NWs (figure 3b). Dominant peaks at 233, 446 and 610 cm−1 are assigned to the Raman active modes of rutilephased TiO2 . The G-band at 1587 cm−1 attributes to the Eg mode of the graphite and is associated with sp2 -bonded configuration, whereas a broad D-band at 1355 cm−1 corresponds to the vibration modes of sp3 -carbon atoms of disordered graphite [26,38]. FTIR spectra of the CQDs/TiO2 NWs are shown in figure 3c. The peak for Ti-O-Ti and Ti-O was present in the range of 600–800 and 1024 cm−1 , respectively [39,40]. The characteristic transmittance peaks of the CQDs/TiO2 NWs at 1648 cm−1 associated with the C=O stretching vibration, indicate the existence of CQDs in the composites [33]. Moreover, the broad peak at 3369 cm−1 was attributed to vibrations of surface adsorbed water [41]. XPS was carried out to investigate the components and surface properties of CQDs/TiO2 NW composite which is shown in figure 4. The full survey spectrum of figure 4a indicates the presence of titanium (Ti 2p), carbon (C 1 s),

................................................

3. Results and discussion

3

rsos.royalsocietypublishing.org R. Soc. open sci. 4: 161051

(PL) spectra were performed using a spectrofluorometer (FP-6200, JASCO). The crystal structure was characterized by Raman spectroscopy (Nanofinder 30, Tokyo Instruments, INC) with a 488 nm laser. The Fourier transform infrared (FTIR) spectroscopy spectra were recorded using a FTIR spectrometer (BRUKER/Vertex 70 V). X-ray photoelectron spectroscopy (XPS) data were obtained with a ULVACPHI, PHI 5000 VersaProbe/Scanning ESCA Microprobe. Fitting of the XPS data was accomplished using XPSPEAK41 software. The measurement of photocurrent was carried out using a three-electrode system. TiO2 NW electrode with or without CQDs was the working electrode; an Ag/AgCl electrode in 3 M KCl was the reference electrode; the Pt sheet was used as the counter electrode. All electrodes were examined in 0.5 M Na2 SO4 solution with a PARSTAT 2263 Advanced Electrochemical System under illumination using a Newport solar simulator with AM 1.5 G (100 mW cm−2 ). Before the experiment, the electrolyte was purged by argon to remove the dissolved oxygen. The SIGMASCAN PRO 5 software was used to calculate the particle size of CQDs and the measured area of working electrode for calculating photocurrent density. The electrochemical impedance spectroscopy (EIS) was measured by applying the open-circuit voltage under 1 sun illumination and recorded over the frequency range of 200 kHz– 100 mHz with ac amplitude of 10 mV by using a PARSTAT 2263 Advanced Electrochemical System. EIS results were analysed and fit using the software program ZVIEW.

1st

(a)

2nd

4th

5th

400

500 600 wavelength (nm)

700

4 ................................................

rsos.royalsocietypublishing.org R. Soc. open sci. 4: 161051

3rd

graphite rod 1

(b)

(c)

intensity (arb. units)

absorbance (arb. units)

graphite rod 2

425 450 475 500 525 550 575 600 625 650 675 wavelength (nm)

(d )

300

800

(e) 0.323 nm

20 nm

10 nm

Figure 1. (a) Photos of as-prepared CQD water solution under UV light (365 nm), in which the sample was obtained after 3500 CV scan cycles on two types of graphite-coated rods. (b) UV-Vis spectrum and (c) PL spectrum of CQD solution. (d,e) HRTEM images of CQDs.

and oxygen (O 1 s) in the CQDs/TiO2 NW composites. The Ti 2p spectra were deconvoluted and resolved into four spin orbit components at 2p3/2 binding energies 457.6, 458.14 eV and their corresponding 2p1/2 components (463.21, 464.0 eV) which are assigned as Ti3+ (TiOOH/coordinatively unsaturated) and Ti4+ (TiO2 ), respectively [42,43]. The large ratio of Ti3+ is suggested owing to the increased electron content of the lattice surface of TiO2 within the voltage-driven reduction process [44]. The peaks at 284.24, 285.44 and 287.99 eV for C 1 s spectrum are ascribed to the C–C bond with sp2 orbital, C–O and C=O bonds, respectively. The main peak of O 1 s spectrum at 529.06, 530.49 and 531.49 eV is attributed to Ti=O, C=O and C–OH, respectively [45,46]. Measurements of linear sweep voltammogram (LSV) and photocurrent density versus elapsed time (I–t) of CQDs/TiO2 NWs and as-prepared TiO2 NW devices were carried out under AM 1.5 G sunlight

experiment simulation

CQD(aq) + DMPO

5 ................................................

rsos.royalsocietypublishing.org R. Soc. open sci. 4: 161051

before UV irradiation 365 nm UV irradiation for 90 s

3430 3440 3450 3460 3470 3480 3490 3500 3510 3520 3530 magnetic field (G)

Figure 2. EPR signals of hydroxyl radical obtained under irradiation of 365 nm on sp2 -CQD solution in the presence of DMPO for 90 s. Inset: simulation of this signal after irradiation by EasySpin toolbox in MATLAB software with magnetic parameters: g = 2.0051; AN = 14.85 G; and AH = 15.12 G. Instrumental settings for detection: frequency, 9.774 GHz; power, 5.044 mW; receiver gain, 8.93 × 10−3 ; modulation amplitude, 2 G; time constant, 40.96 ms; resolution, 2048 points.

(b)

(a)

CQDs/TiO2NW

intensity (arb. units)

TiO2NW

Eg

A1g

D

G

50 nm 200

400

600

800 1000 1200 1400 1600 1800 Raman shift (cm–1)

(c) transmittance (arb. units)

CQDs/TiO2NW TiO2NW

1648 3369 1024 600–800 800 1200 1600 2000 2400 2800 3200 3600 4000 wavenumber (cm–1)

Figure 3. (a) HRTEM of CQD/TiO2 NWs; (b) Raman spectra; and (c) FTIR spectra of TiO2 NWs and CQDs/TiO2 NWs.

(a)

(b)

6

intensity (arb. units)

Ti 2p Ti3+ Ti4+ Ti4+

C 1s

800 700 600 500 400 300 200 100

0

(c)

466

464

462

460

458

456

454

(d) C–C

intensity (arb. units)

468

C=O

O 1s

C 1s Ti=O

C=O

C–O C–OH

290

288

286 284 282 binding energy (eV)

280

538 536 534 532 530 528 526 524 binding energy (eV)

Figure 4. XPS spectra of CQDs/TiO2 NWs. (a) Full survey. (b) Ti 2p spectra. (c) C 1 s spectra. (d) O 1 s spectra.

illumination, as shown in figure 5a,b. It is important to note that a photocurrent density of 160 μA cm−2 at 0 V versus Ag/AgCl for CQDs/TiO2 NWs was remarkably obtained and a net enhancement ratio of 6.4 was achieved when compared with the as-prepared TiO2 electrode (25 µA cm−2 ). From figure 5b, both of two photoanode devices represented good reproducibility and stability as the illumination was continually turned on and off. Furthermore, the sharp spike in the photocurrent during the on/off illumination cycles demonstrates the predominant transport of photo-generated electron in the CQDs/TiO2 NWs. The increased photocurrent of CQDs/TiO2 NWs may be attributed to the effect of synergetic photocatalytic behaviour and peroxidase-like property of CQDs which facilitate charge separation/transportation during the water splitting process. In order to verify our suggestions, the study of EIS of interfacial electron transfer of CQDs/TiO2 NWs is highlighted in figure 5c. EIS spectra show that both photoanodes revealed an obvious semicircle of Nyquist plot at the high frequencies and a Warburg type line at low frequencies under illumination [47]. The equivalent circuit modes applied to fit the experimental EIS data of the as-prepared TiO2 NWs and the CQDs/TiO2 NW composite electrode is shown in the inset of figure 5c. The fitting results of all parameters of the equivalent circuit are listed in table 1. It should be noted that a larger charge transfer resistance (Rct) for TiO2 electrode (520.6 Ω) was observed when compared with that of the CQDs/TiO2 NW electrode (337.9 Ω). In addition, the Warburg resistance for the CQDs/TiO2 NW electrode (1273 Ω) is apparently smaller than that of the TiO2 electrode (4921 Ω). From EIS analysis, it demonstrated that CQDs/TiO2 NWs exhibit predominant electron transport property and ionic conduction at the interfacial heterojunction of CQDs/TiO2 NWs and it could be attributed to the synergetic photocatalytic behaviour and peroxidase property of CQDs. The proposed scheme of decomposition of H2 O2 by peroxidase-like CQDs is shown in figure 5d. Upon solar illumination on CQDs/TiO2 NWs, photo-generated carriers were separated into photo-generated electrons (e− ) and photo-generated holes (h+ ). The e− and h+ react with adsorbed oxidants/reducers (O2 /OH− ) to produce photo-reactive oxygen radicals (1 O2 , •OH) which play the key role in the decomposition of the H2 O2 intermediates, which is in good agreement with the EPR study (electronic supplementary material, figure S4) [48,49].

................................................

Ti 2p Ti3+

rsos.royalsocietypublishing.org R. Soc. open sci. 4: 161051

O 1s

(b) 300 photocurrent (mA cm–2)

CQDs/TiO2 NW

200 150 100 50 0 –0.6

350 300 250 200 150 100 50 0

–0.3

0 0.3 voltage (V) Rs

–1400

0 30 60 90 120 150 180 210 240 270 300 330 elapsed time (s)

0.9

CPE Rct

–1200

0.6

H2O2

(d) Rw 5

–1000 1O

–800 e–

–600 H2O

–400

0

400

800

1200 1600 2000 2400 Zre (W)

O2

CQD* + + +

2e–

–200 0

2 – e– e

TiO2

Figure 5. (a) LSV curve (b) I–t curve and (c) Nyquist plot of TiO2 NWs and CQDs/TiO2 NWs under AM 1.5 G sunlight illumination. (d) Proposed scheme of decomposition of H2 O2 by peroxidase-like CQDs on TiO2 NWs. (EPR study of the decomposition of H2 O2 by CQDs was illustrated in the electronic supplementary material, figure S4.) Table 1. EIS fitting parameters of as-prepared TiO2 NWs and CQDs/TiO2 NWs. description

parameters

TiO2 NWs

CQDs/TiO2 NW

unit

Ohmic series resistance

Rs

216.9

304.9

Ω

charge transfer resistance at electrode/electrolyte interface

Rct

520.6

.........................................................................................................................................................................................................................

Ω

337.9

.........................................................................................................................................................................................................................

−5

−6

CPE for capacitance of electrode

CPE

1.89×10

1.90×10

F · sn−1

Warburg impedance

Rw

4921

1273

Ω

......................................................................................................................................................................................................................... .........................................................................................................................................................................................................................

4. Conclusion In summary, for the first time to our knowledge, the CQDs with a size less than 5 nm in water solution have been synthesized by the one-step electrochemical method without using chemicals and further post-treatments. For enhancing the water splitting photocurrent, CQDs/TiO2 NWs are used to construct a synergetic semiconductor as a hybrid photoanode. A remarkable enhancement by 6.4 times on water splitting current was observed which is attributed to CQDs which served as an efficient catalyst for decomposing H2 O2 , resulting in a reduced interfacial charge transferred resistance and fast ion diffusions. The green synthesis CQDs and CQDs/TiO2 NWs may open a new way to design a broad range of photoelectric materials for application in bioscience and new energy-saving technology. Data accessibility. The datasets supporting this article have been uploaded as part of the electronic supplementary material.

Authors’ contributions. Y.-C.Y. and C.-C.L. performed the experiments and collected data. P.-Y.C. performed the EPR experiments. Y.-C.Y. conceived and designed the synthesis of CQDs. Y.-C.Y., W.-Y.K. and K.-J.L. coordinated the study and wrote the manuscript. T.R.T. drew figure 5d. All authors gave final approval for publication . Competing interests. The authors declare no competing interests.

................................................

TiO2 NW

250

(c) –1600

Zimg (W)

7

400

rsos.royalsocietypublishing.org R. Soc. open sci. 4: 161051

photocurrent density (mA cm–1)

(a)

Funding. This work is supported by the Ministry of Science and Technology of Taiwan (MOST 104-2113-M-005-011MY3).

13. Dubé CE, Wright DW, Armstrong WH. 2000 Evidence for cooperativity in the disproportionation of H2 O2 efficiently catalyzed by a tetranuclear manganese complex. Angew. Chem. 112, 2253–2256. (doi:10.1002/1521-3757(20000616)112:123.0.CO;2-R) 14. Çıçek E, Dede B. 2014 Efficiencies of the Copper (II) adsorbed zeolites in the H2 O2 disproportionation reaction. Acta Phys. Polonica A 125, 872–874. (doi:10.12693/APhysPolA.125.872) 15. Shaker AM, Awad AM, Adam MSS. 2006 Salt effects on reactivity of some Fe(II)-Azo complexes catalyzing disproportionation of hydrogen peroxide. Monatshefte für Chemie/Chemical Monthly 137, 421–431. (doi:10.1007/s00706-005-0432-6) 16. Sayama K, Arakawa H. 1997 Effect of carbonate salt addition on the photocatalytic decomposition of liquid water over Pt-TiO2 catalyst. J. Chem. Soc. Faraday Trans. 93, 1647–1654. (doi:10.1039/ A607662I) 17. Munuera G, Espinos JP, Fernandez A, Malet P, Gonzalez-Elipe AR. 1990 TiO2 corrosion during water photocleavage using Rh/TiO2 suspensions. J. Chem. Soc. Faraday Trans. 86, 3441–3445. (doi:10.1039/ FT9908603441) 18. Yu X, Liu R, Zhang G, Cao H. 2013 Carbon quantum dots as novel sensitizers for photoelectrochemical solar hydrogen generation and their size-dependent effect. Nanotechnology 24, 335401. (doi:10.1088/0957-4484/24/33/335401) 19. Zhang Z, Zheng T, Li X, Xu J, Zeng H. 2016 Progress of carbon quantum dots in photocatalysis applications. Particle Particle Syst. Characteriz. 33, 457–472. (doi:10.1002/ppsc.201500243) 20. Ong W-J, Putri LK, Tan Y-C, Tan L-L, Li N, Ng YH, Wen X, Chai S-P. In press. Unravelling charge carrier dynamics in protonated g-C3 N4 interfaced with carbon nanodots as co-catalysts toward enhanced photocatalytic CO2 reduction: a combined experimental and first-principles DFT study. Nano Res. 1–24. (doi:10.1007/s12274-016-1391-4) 21. Zhu S, Song Y, Zhao X, Shao J, Zhang J, Yang B. 2015 The photoluminescence mechanism in carbon dots (graphene quantum dots, carbon nanodots, and polymer dots): current state and future perspective. Nano Res. 8, 355–381. (doi:10.1007/s12274-0140644-3) 22. Wang R, Lu K-Q, Tang Z-R, Xu Y-J. 2017 Recent progress in carbon quantum dots: synthesis, properties and applications in photocatalysis. J. Mat. Chem. A 5, 3717–3734. (doi:10.1039/ C6TA08660H) 23. Himaja AL, Karthik PS, Singh SP. 2015 Carbon dots: the newest member of the carbon nanomaterials family. Chem. Record 15, 595–615. (doi:10.1002/tcr. 201402090) 24. Wang Y, Hu A. 2014 Carbon quantum dots: synthesis, properties and applications. J. Mat. Chem. C 2, 6921–6939. (doi:10.1039/C4TC00988F) 25. Wang Y et al. 2011 Carbon dots of different composition and surface functionalization: cytotoxicity issues relevant to fluorescence cell

26.

27.

28.

29.

30.

31.

32.

33.

34.

35.

36.

37.

38.

imaging. Exp. Biol. Med. 236, 1231–1238. (doi:10.1258/ebm.2011.011132) Kang Z, Wang E, Mao B, Su Z, Chen L, Xu L. 2005 Obtaining carbon nanotubes from grass. Nanotechnology 16, 1192. (doi:10.1088/09574484/16/8/036) Wu L et al. 2013 Surface passivation of carbon nanoparticles with branched macromolecules influences near infrared bioimaging. Theranostics 3, 677–686. (doi:10.7150/thno.6535) Zhu W, Zhang J, Jiang Z, Wang W, Liu X. 2014 High-quality carbon dots: synthesis, peroxidase-like activity and their application in the detection of H2 O2 , Ag+ and Fe3+ . RSC Adv. 4, 17 387–17 392. (doi:10.1039/C3RA47593 J) Lim SY, Shen W, Gao Z. 2015 Carbon quantum dots and their applications. Chem. Soc. Rev. 44, 362–381. (doi:10.1039/C4CS00269E) Zhou Z, Shen Y, Li Y, Liu A, Liu S, Zhang Y. 2015 Chemical cleavage of layered carbon nitride with enhanced photoluminescent performances and photoconduction. ACS Nano. 9, 12 480–12 487. (doi:10.1021/acsnano.5b05924) Li H et al. 2010 Water-soluble fluorescent carbon quantum dots and photocatalyst design. Angew. Chem. Int. Ed. 49, 4430–4434. (doi:10.1002/anie. 200906154) Tian J, Leng Y, Zhao Z, Xia Y, Sang Y, Hao P, Zhan J, Li M, Liu H. 2015 Carbon quantum dots/hydrogenated TiO2 nanobelt heterostructures and their broad spectrum photocatalytic properties under UV, visible, and near-infrared irradiation. Nano Energy 11, 419–427. (doi:10.1016/j.nanoen.2014. 10.025) Hui D, Peng Z, Tian-Yi W, Ji-Lie K, Huan-Ming X. 2014 Nitrogen-doped carbon dots derived from polyvinyl pyrrolidone and their multicolor cell imaging. Nanotechnology 25, 205604. (doi:10.1088/0957-4484/25/20/205604) Wang DM, Gao MX, Gao PF, Yang H, Huang CZ. 2013 Carbon nanodots-catalyzed chemiluminescence of luminol: a singlet oxygen-induced mechanism. J. Phys. Chem. C 117, 19 219–19 225. (doi:10.1021/jp404973b) Ge J et al. 2014 A graphene quantum dot photodynamic therapy agent with high singlet oxygen generation. Nat. Commun. 5, 4596. (doi:10.1038/ncomms5596) Christensen H, Sehested K, Corfitzen H. 1982 Reactions of hydroxyl radicals with hydrogen peroxide at ambient and elevated temperatures. J. Phys. Chem. 86, 1588–1590. (doi:10.1021/ j100206a023) Bilski P, Reszka K, Bilska M, Chignell CF. 1996 Oxidation of the spin trap 5,5-dimethyl-1-pyrroline N-oxide by singlet oxygen in aqueous solution. J. Am. Chem. Soc. 118, 1330–1338. (doi:10.1021/ ja952140s) Ming H, Ma Z, Liu Y, Pan K, Yu H, Wang F, Kang Z. 2012 Large scale electrochemical synthesis of high quality carbon nanodots and their photocatalytic

................................................

1. Kar M, Basak A. 2007 Design, synthesis, and biological activity of unnatural enediynes and related analogues equipped with pH-dependent or phototriggering devices. Chem. Rev. 107, 2861–2890. (doi:10.1021/cr068399i) 2. Yubin C, Chi-Hung C, Zhixiao Q, Shaohua S, Tennyson D, Clemens, B. 2017 Electron-transfer dependent photocatalytic hydrogen generation over cross-linked CdSe/TiO2 type-II heterostructure. Nanotechnology 28, 084002. (doi:10.1088/13616528/aa5642) 3. Ren R, Wen Z, Cui S, Hou Y, Guo X, Chen, J. 2015 Controllable synthesis and tunable photocatalytic properties of Ti3+ -doped TiO2 . Sci. Rep. 5, 10714. (doi:10.1038/srep10714) 4. Ong W-J, Tan L-L, Chai S-P, Yong S-T, Mohamed AR. 2014 Highly reactive {001} facets of TiO2 -based composites: synthesis, formation mechanism and characterization. Nanoscale 6, 1946–2008. (doi:10.1039/C3NR04655A) 5. Chun-Ren K, Jyun-Sheng G, Yen-Hsun S, Jyh-Ming T. 2016 The effect of silver nanoparticles/ graphene-coupled TiO2 beads photocatalyst on the photoconversion efficiency of photoelectrochemical hydrogen production. Nanotechnology 27, 435405. (doi:10.1088/09574484/27/43/435405) 6. Ong WJ, Tan LL, Chai SP, Yong ST, Mohamed AR. 2014 Facet-dependent photocatalytic properties of TiO2 -based composites for energy conversion and environmental remediation. ChemSusChem 7, 690–719. (doi:10.1002/cssc.201300924) 7. Ong W-J, Tan L-L, Chai S-P, Yong S-T, Mohamed AR. 2014 Self-assembly of nitrogen-doped TiO2 with exposed {001} facets on a graphene scaffold as photo-active hybrid nanostructures for reduction of carbon dioxide to methane. Nano Res. 7, 1528–1547. (doi:10.1007/s12274-014-0514-z) 8. Pan X, Yang M-Q, Fu X, Zhang N, Xu Y-J. 2013 Defective TiO2 with oxygen vacancies: synthesis, properties and photocatalytic applications. Nanoscale 5, 3601–3614. (doi:10.1039/C3NR0 0476G) 9. Liu J et al. 2015 Metal-free efficient photocatalyst for stable visible water splitting via a two-electron pathway. Science 347, 970–974. (doi:10.1126/ science.aaa3145) 10. Graetzel M. 1981 Artificial photosynthesis: water cleavage into hydrogen and oxygen by visible light. Acc. Chem. Res. 14, 376–384. (doi:10.1021/ar0007 2a003) 11. Liu J, Zhang Y, Lu L, Wu G, Chen W. 2012 Self-regenerated solar-driven photocatalytic water-splitting by urea derived graphitic carbon nitride with platinum nanoparticles. Chem. Commun. 48, 8826–8828. (doi:10.1039/ C2CC33644H) 12. Ni M, Leung MK, Leung DY, Sumathy K. 2007 A review and recent developments in photocatalytic water-splitting using TiO2 for hydrogen production. Renew. Sust. Energy Rev. 11, 401–425. (doi:10.1016/ j.rser.2005.01.009)

rsos.royalsocietypublishing.org R. Soc. open sci. 4: 161051

References

8

39.

42.

46. Yu X, Liu J, Yu Y, Zuo S, Li B. 2014 Preparation and visible light photocatalytic activity of carbon quantum dots/TiO2 nanosheet composites. Carbon 68, 718–724. (doi:10.1016/j.carbon.2013.11.053) 47. Bessekhouad Y, Brahimi R, Hamdini F, Trari M. 2012 Cu2 S/TiO2 heterojunction applied to visible light Orange II degradation. J. Photochemistry Photobiol. A Chem. 248, 15–23. (doi:10.1016/j.jphotochem. 2012.08.013) 48. Reszka K, Bilski P, Chignell CF. 1992 EPR spectra of DMPO spin adducts of superoxide and hydroxyl radicals in pyridine. Free Radical Res. Commun. 17, 377–385. (doi:10.3109/10715769209083142) 49. Shi W, Wang Q, Long Y, Cheng Z, Chen S, Zheng H, Huang Y. 2011 Carbon nanodots as peroxidase mimetics and their applications to glucose detection. Chem. Commun. 47, 6695–6697. (doi:10.1039/C1CC11943E)

9 ................................................

41.

inactivation in the dark and under light irradiation. Interface Focus 5, 20140046. (doi:10.1098/rsfs. 2014.0046) 43. Antony RP, Mathews T, Dash S, Tyagi AK, Raj B. 2012 X-ray photoelectron spectroscopic studies of anodically synthesized self-aligned TiO2 nanotube arrays and the effect of electrochemical parameters on tube morphology. Mat. Chem. Phys. 132, 957–966. (doi:10.1016/j.matchemphys.2011. 12.041) 44. Myung J-H, Neagu D, Miller DN, Irvine JTS. 2016 Switching on electrocatalytic activity in solid oxide cells. Nature 537, 528–531. (doi:10.1038/nature 19090) 45. Pan J, Sheng Y, Zhang J, Wei J, Huang P, Zhang X, Feng B. 2014 Preparation of carbon quantum dots/ TiO2 nanotubes composites and their visible light catalytic applications. J. Mat. Chem. A 2, 18 082–18 086. (doi:10.1039/C4TA03528C)

rsos.royalsocietypublishing.org R. Soc. open sci. 4: 161051

40.

property. Dalton Trans. 41, 9526–9531. (doi:10.1039/C2DT30985H) Vasconcelos DCL, Nunes EHM, Gasparon M, Vasconcelos WL. 2011 Infrared spectroscopy of titania sol-gel coatings on 316 L stainless steel. Mat. Sci. Appl. 2, 1375. (doi:10.4236/msa.2011.210186) Zhao CE, Wang WJ, Sun D, Wang X, Zhang JR, Zhu JJ. 2014 Nanostructured graphene/TiO2 hybrids as high-performance anodes for microbial fuel cells. Chem. Eur. J. 20, 7091–7097. (doi:10.1002/chem. 201400272) Madejová J, Janek M, Komadel P, Herbert H-J, Moog H. 2002 FTIR analyses of water in MX-80 bentonite compacted from high salinary salt solution systems. Appl. Clay Sci. 20, 255–271. (doi:10.1016/S01691317(01)00067-9) Rtimi S, Nesic J, Pulgarin C, Sanjines R, Bensimon M, Kiwi J. 2015 Effect of surface pretreatment of TiO2 films on interfacial processes leading to bacterial